金威E2594T1-1不銹鋼藥芯焊絲 2594雙相氣保

時間：2024-07-16

作者：河北坤旺焊接材料有限公司

類別

牌號

AWS A5.22

GB/T 17853

熔敷金屬化學成分(wt.%)

熔敷金屬力學性能

其它

Rm(MPa)

A(%)

E307T1-1

TS307-FC11

≤0.13

≤1.0

3.30-4.75

≤0.04

≤0.03

18.0-20.5

9.0-10.5

0.5-1.5

≤0.75

—

≥590

≥30

E308LT1-1

TS308L-FC11

≤0.04

≤1.0

0.5-2.5

≤0.04

≤0.03

18.0-21.0

9.0-11.0

≤0.75

—

≥520

≥30

E308HT1-1

TS308H-FC11

0.04-0.08

≤1.0

0.5-2.5

≤0.04

≤0.03

18.0-21.0

9.0-11.0

≤0.75

—

≥550

≥30

E309LT1-1

TS309L-FC11

≤0.04

≤1.0

0.5-2.5

≤0.04

≤0.03

22.0-25.0

12.0-14.0

≤0.75

—

≥520

≥30

E309HT1-1

TS309H-FC11

0.04-0.10

≤1.0

0.5-2.5

≤0.04

≤0.03

22.0-25.0

12.0-14.0

≤0.75

—

≥550

≥30

E309LMoT1-1

TS309LMo-FC11

≤0.04

≤1.0

0.5-2.5

≤0.04

≤0.03

21.0-25.0

12.0-16.0

2.0-3.0

≤0.75

—

≥520

≥25

E316LT1-1

TS316L-FC11

≤0.04

≤1.0

0.5-2.5

≤0.04

≤0.03

17.0-20.0

11.0-14.0

2.0-3.0

≤0.75

—

≥485

≥30

E317LT1-1

TS317L-FC11

≤0.04

≤1.0

0.5-2.5

≤0.04

≤0.03

18.0-21.0

12.0-14.0

3.0-4.0

≤0.75

—

≥520

≥20

E347LT1-1

E347T1-1

TS347L-FC11

≤0.04

≤1.0

0.5-2.5

≤0.04

≤0.03

18.0-21.0

9.0-11.0

≤0.75

Nb: 8×C-1.0

≥520

≥25

E347T1-1

TS347-FC11

≤0.08

≤1.0

0.5-2.5

≤0.04

≤0.03

18.0-21.0

9.0-11.0

≤0.75

Nb: 8×C-1.0

≥520

≥30

E310T1-1

TS310-FC11

≤0.20

≤1.0

1.0-2.5

≤0.04

≤0.03

25.0-28.0

20.0-22.5

≤0.75

—

≥550

≥30

E2209T1-1

TS2209-FC11

≤0.04

≤1.0

0.5-2.0

≤0.04

≤0.03

21.0-24.0

7.5-10.0

2.5-4.0

≤0.75

N: 0.08-0.20

≥690

≥20

E2594T1-1

TS2594-FC11

≤0.04

≤1.0

0.5-2.5

≤0.04

≤0.03

24.0-27.0

8.0-10.5

2.5-4.5

≤0.75

N: 0.20-0.30

W: ≤1.0

≥760

≥15

E410T1-1

TS410-FC11

≤0.12

≤1.0

≤1.2

≤0.04

≤0.03

11.0-13.5

≤0.6

≤0.75

—

≥520

≥20

E410NiMoT1-1

TS410NiMo-FC11

≤0.06

≤1.0

≤0.04

≤0.03

11.0-12.5

4.0-5.0

0.4-0.7

≤0.75

—

≥760

≥15

E308LT1-4

TS308L-11

≤0.04

≤1.0

0.5-2.5

≤0.04

≤0.03

18.0-21.0

9.0-11.0

≤0.75

—

≥520

≥30

E308HT1-4

TS308H-11

0.04-0.08

≤1.0

0.5-2.5

≤0.04

≤0.03

18.0-21.0

9.0-11.0

≤0.75

—

≥550

≥30

E309LT1-4

TS309L-11

≤0.04

≤1.0

0.5-2.5

≤0.04

≤0.03

22.0-25.0

12.0-14.0

≤0.75

—

≥520

≥30

E309HT1-4

TS 309H-11

0.04-0.10

≤1.0

0.5-2.5

≤0.04

≤0.03

22.0-25.0

12.0-14.0

≤0.75

—

≥550

≥30

E309LMoT1-4

TS309LMo-11

≤0.04

≤1.0

0.5-2.5

≤0.04

≤0.03

21.0-25.0

12.0-16.0

2.0-3.0

≤0.75

—

≥520

≥25

E316LT1-4

TS316L-11

≤0.04

≤1.0

0.5-2.5

≤0.04

≤0.03

17.0-20.0

11.0-14.0

2.0-3.0

≤0.75

—

≥485

≥30

E317LT1-4

TS317L-11

≤0.04

≤1.0

0.5-2.5

≤0.04

≤0.03

18.0-21.0

12.0-14.0

3.0-4.0

≤0.75

—

≥520

≥20

E347LT1-4

TS347L-11

≤0.04

≤1.0

0.5-2.5

≤0.04

≤0.03

18.0-21.0

9.0-11.0

≤0.75

Nb: 8×C-1.0

≥520

≥25

E347T1-4

TS347-11

≤0.08

≤1.0

0.5-2.5

≤0.04

≤0.03

18.0-21.0

9.0-11.0

≤0.75

Nb: 8×C-1.0

≥520

≥30

E2209T1-4

TS2209-11

≤0.04

≤1.0

0.5-2.0

≤0.04

≤0.03

21.0-24.0

7.5-10.0

2.5-4.0

≤0.75

N: 0.08-0.20

≥690

≥20

詞條
詞條說明
YD643氣保護堆焊芯焊絲高硬度焊絲
?YD643氣保護堆焊修復(fù)藥芯焊絲：??說明：YD643為CO2或80Ar+20CO2保護單齒輥堆焊修復(fù)藥芯焊絲。該焊絲焊接工藝性能優(yōu)良，成形美觀，飛濺較小。熔敷金屬為高鉻合金，因而具有優(yōu)良的料磨損性能。同時添加Mo、W、V、B等元素，提高了焊縫金屬高溫性能，加入Ni元素，保證焊縫在不降低性能的條件下，增加抗沖擊性。該焊絲堆焊時會出現(xiàn)細裂紋，是釋放應(yīng)力的結(jié)果，
四川大西洋CHS032R電焊條 A032 317L承壓設(shè)備不銹鋼焊條
說明：CHSO32R是鈦鈣型藥皮的低碳不銹鋼焊條。交直流兩用。由于焊縫中含有較高鉬，對酸、、、醋酸等具有較強的抗腐蝕性能。用途：用于焊接AISI317、Cr10Si3及相同類型的不銹鋼承壓結(jié)構(gòu)件。熔敷金屬化學成分（質(zhì)量分數(shù)）：%CMnSiCrNiMoSPCu標準值≤0.040.5-2.5≤0.9018.0-21.012.0-14.03.0-4.0≤0.75≤ 0.020≤ 0.030―例0.028
大西洋A412焊條批發(fā)四川大西洋CHS412不銹鋼焊條
說明：CHS412是金紅石藥皮類型的Cr26Ni21Mo2純奧氏體不銹鋼焊條。由于焊縫金屬添加了鉬，故耐蝕性、耐熱性、抗裂性均比CHS402、CHS407有所提高?？山恢绷鲀捎?，焊接工藝性能好。用途：用于在高溫下工作的耐熱不銹鋼，也可用于焊接不銹鋼襯里、異種鋼等。在焊接淬硬性高的碳鋼、低合金鋼時韌性好。熔敷金屬化學成分（質(zhì)量分數(shù)）：%CMnSiCrNiMoCuSP標準值≤0.121.0-2.5≤0
斯米克鋁鎂焊絲5556 飛機牌ER5556鋁鎂合金焊絲
說明：5556是含5%鎂及較高錳含量的鋁鎂焊絲，具有高的強度，良好的耐蝕性及抗熱裂性能。焊縫陽化處理后仍為白色，能為焊接接頭提供良好的配色。用途：用于高鎂（≥3%Mg）的鋁合金氬弧焊的材料。焊絲化學成分（%）Mg4.7-5.5MnTiA1Cr余量0.5-1.00.05-0.200.05-0.20物理特性（近似值）線膨脹系數(shù)106/K比重kg/dm3熔化溫度熱導(dǎo)率電導(dǎo)率℃w/m·k%IACS(20-