NANOMETAL INKs are produced by the Gas Evaporation Method. These newly developed inks consist of metal nanoparticles dispersed stably and not aggregated in some organic solvent. The inks enable to form electro-conductive fine patterns directly by printing processes such as ink-jet printing.

Nano Metal Ink

Name of Products	Au-Nanometal Ink	Ag-Nanometal Ink	Ag-Nanometal Ink
(Low temperature type)	ITO Nanometal Ink
Type of Number	Au1T	Ag1T	Ag1teH	L-Ag1T	L-Ag1TeH	ITO 1Cden
For Ink Jet	X	X	○	X	○	○
Metal Content (wt%)	30	30	55?60	30	55?60	20
Sovlent	Toluene	Toluene	Tetradecane	Toluene	Tetradecane	Cyclododecene
Adhesive Inproving
Additives	–	–	–	–	–	–
Average Particle
Size (mm)	3?7
Viscocity (mPa·s)	<5	<5	5?15	<5	5?15	5?15
Cured-film performance below is a refference only, NOT guaranteed
Curing Condition	350℃x30min or
300℃x30min	220℃x30min	150℃x60min	*1
Layer After Curing
(μm)	<1	<1	<1	<1	<1	–
Resistivity (μΩ·cm)	350℃x30min:
8?10
300℃x30min:
12?15	approx. 3	approx. 3	approx. 10	–
Substrates to be used	350℃x30min:8?10
300℃x30min:12?15	Heat-resistant temperature of substrates should be higher than curing temperature.
Adhesive Strength
(kg/mm2)	<1	<1	<1	<1	<1	>2
*1 230℃x10min in 8Pa in vacuum + 230℃x60min in air

詞條
詞條說明
疏水干膜光刻膠Hydrophobic Dry Film Photoresist
疏水干膜光刻膠Hydrophobic Dry Film Photoresist Hydrophobic Dry Film Photoresist Material Dry Film total Thickness Color, Tint Glass Transition (°C) H2O Contact Angle, 23°C Minimum Resolution, μ Maximum Aspec
無鉛琺瑯釉
無鉛琺瑯釉我司供應供應德國無鉛琺瑯釉，適用于**首飾，手表，珠寶，陶瓷，餐具，玻璃藝術加工等，750度燒結(jié)，色彩豐富。我司供應無鉛珠寶琺瑯釉料，紅寶石琺瑯釉，陶瓷釉，玻璃釉筆等，色彩齊全多樣 Our range of glass enamel pens is another example of a productthat derived from an industrial applicat
醫(yī)用電極和生物傳感器-
醫(yī)用電極和生物傳感器對于醫(yī)療電子產(chǎn)品，可靠性和可靠性至關重要。患者舒適，侵入性小，一次性產(chǎn)品和遠程診斷正在推動醫(yī)療電子領域的發(fā)展。生物傳感器，例如葡萄糖試紙， EKG /ECG電極，用于刺激肌肉的TENS墊，用于藥物輸送的離子電滲療法墊以及無數(shù)其他醫(yī)療用途電子應用依賴于gzyb油墨來提供準確性，可靠性和兼容性。制定兼容隨著人體以及各種交互式醫(yī)療凝膠和化學藥品的出現(xiàn)，gzyb**的墨水正在使
UV壓敏膠（PSA）
廣州銀標供應： UV壓敏膠（PSA）如果經(jīng)過溶液涂布、干燥和化學反應制作的PSA中可能會殘留溶劑等有害化學品。但用UV固化方式制作PSA，將無溶劑的液態(tài)成分通過UV光照射聚合而成。污染低，簡化生產(chǎn)，提高生產(chǎn)效率。UV復合膠傳統(tǒng)高阻隔包裝材料制作的軟包裝，幾乎都是溶劑型粘合劑，溶劑量＞70%。水性粘合劑雖然無溶劑，但干燥慢，生產(chǎn)效率低，對塑料的粘接性能也不好。UV膠粘劑不含溶劑，無揮發(fā)，無有害殘留物